The work is devoted to the study of the formation of structure and mechanical characteristics of the laminated composites of the system Ti-Al and Ti-Al-Me with high specific strength and moderate heat resistance. The investigation of a microstructure of the composite sample showed that it consists of a solid solution of aluminum in titanium, zirconium, and intermetallic layers Ti3Al, TiAl, TiAl2 and TiAl3. Results of short-term tests on 3 point bending showed that the average values of tensile strength of alloy composites are at the level 820 MPa and 993 MPa, and the doped composite - 952 MPa and 1352 MPa at temperatures of 20 and 700 °C, respectively.